It is created from electrical glass cloth with alkali-free that has been impregnated with BMI resin under pressure. heat and rolling. The thermal grade is class H insulation. With excellent mechanical strength and dielectric property, radiation-proof. Used for the insulating slots. windings. gaskets. junction board of the dry-type transformer/mine transformer/railway transformer/electrical equipment/traction motor etc.
BMI glass cloth laminated, epoxy pre-impregnated DMD laminate
Sheets: thickness 0.5-200mm size:1000X2000mm
Technical data
No Specification Unit Index
1 Density g/cm2 >= 1.80
2 Marin temperature, lengthwise oC >= 280
3 Flexural strength, At room temperature Mpa >= 343.1
lengthwise 180 oC >= 176.5
4 Bonding strength N >= 4900
5 Impact strength, lengthwise KJ/ M2 >= 147
Surface At room temperature >= 1.0X10 6
6 resistively After wet M Ω m >= 1.0X10 4
180 oC >= 1.0X10 4
At room temperature >= 1.0X10 5
7 Volume resistively After wet M Ω m >= 1.0X10 3
180 oC >= 1.0X10 3
8 Dissipation factor <= 0.05
Electrical strength perpendicular 0.5-1mm >= 22
9 to lamination in transformer oil at 1.2-2mm MV/m >= 20
90 oC 2.1-3mm >= 18
10 Insulation resistivity para At room
llel to lamination temperature >= M Ω >= 1.0X10 4
After wet >= 1.0X10 2
11 Breakdown voltage parallel to lamination in KV >= 30
transformer oil at 90 oC+- 2 oC